2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance

    Buy cheap 2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance from wholesalers
     
    Buy cheap 2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance from wholesalers
    • Buy cheap 2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance from wholesalers
    • Buy cheap 2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance from wholesalers
    • Buy cheap 2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance from wholesalers

    2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance

    Ask Lasest Price
    Brand Name : HUITIAN
    Model Number : 2810
    Price : Negotiation
    Payment Terms : L/C, T/T
    Supply Ability : 25,000 KG/M
    Delivery Time : 8-15 days
    • Product Details
    • Company Profile

    2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance

    2810 TDS-EN-R.pdf

    Huitian® 2810 rubber repair agent is a three-component RT-vulcanized PU adhesive that requires no heating. It has high bonding strength with metal, rubber, and fabric, and features medium hardness, resistance to wear, corrosion, impact and aging, and good elasticity.

    Typical Applications
    Repair of local defects on conveyor belts, cables, rollers, and other components; serving as insulation seal of cable joints, cold vulcanization protective layer of rubber conveyor belt joints, and lining coating against equipment cavitation. No special heating and pressure device required, for RT vulcanization. Good aging resistance, and excellent resistance to high and low temperatures.

    Properties before Curing

    Typical value Range

    Part A
    Appearance Colorless viscous liquid
    Chemical composition Polyurethane
    Density (g/cm3) (GB/T13354-1992) 1.10 1.08~1.11

    Part B
    Appearance Black viscous liquid
    Chemical composition Coupling agent
    Density (g/cm3) (GB/T13354-1992) 1.10 1.08~1.11

    Treating agent
    Appearance Light yellow liquid

    Mixing Properties

    Typical value Range
    Appearance Black clay
    Mixing weight ratio A:B=3:1
    Pot life (min) 4 3~12
    (100g@25℃)
    Full curing time (h) 2 1.5~2.5
    (100g@25℃)

    Properties after Curing

    Typical value Range
    Tensile strength (MPa) 32 >25
    (GB/T528-1998)
    Peel strength (N/2.5cm) 10 >8
    (GB/T2791-1995)
    Impact strength (J/cm2) 2.0 >1.8
    Elongation at break (%) 350 300~400
    (GB/T528-1998)
    Working temperature (℃) -60~85

    Directions for Use
    1. Use a tungsten steel grinding disc to roughen the surface of the broken rubber of the conveyor belt. Be careful not to polish or burn when grinding.
    2. Use a cleaning agent to clean the surface dirt and residues after treatment until there is no dirt left in the cleaning agent, and then dry it naturally or heat it.
    3. Apply a layer of rubber primer evenly on the treated rubber surface and dry it naturally or by heating.
    4. Prepare the glue according to the weight ratio of A: B=20:1 and stir it quickly and evenly within 1 minute. Use it up within the operation period and prepare it as needed.
    5. Use a short-bristled brush or a rubber scraper to apply the prepared glue to the treated glue surface. The thickness of each application should be controlled at about 1mm, and the total thickness should be controlled within 2mm.

    Cautions
    1. After Part A and Part B are well stirred, they must be used up within pot life.
    2. When the temperature is low, proper heating can improve operability.
    Please consult the MSDS of the product for safety information.

    Packing Specification
    Order code: 281003, 500 g/set, 1 set/box, 10 sets/carton

    Storage
    Store at 8~28°C in a cool and dry place.
    The shelf life is 10 months.



    HUITIAN Profile


    Quality 2810 Rubber Repair Agent Repair Of Local Defects On Conveyor Belts, Cables, Rollers And Other Components Good Aging Resistance, Excellent Resistance for sale
    Inquiry Cart 0
    Send your message to this supplier
     
    *From:
    *To: Shanghai Huitian New Material Co., Ltd
    *Subject:
    *Message:
    Characters Remaining: (0/3000)